[[File:Mace wiki.png|thumb|Cross sectional view of a silicon wafer after metal assisted chemical etching (MACE). The dissolution rate of silicon is locally enhanced due to silver nanoparticles initially deposited at the surface. Eventually the silver nanoparticles "sink" into the wafer leaving behind columnar pores.]]

'''Metal Assisted Chemical Etching''' (also known as MACE) is the process of wet chemical [[etching]] of [[semiconductors]] (mainly [[silicon]]) with the use of a [[metal]] [[catalyst]], usually deposited on the surface of a [[semiconductor]] in the form of a thin film or [[nanoparticle]]s. The semiconductor, covered with the metal is then immersed in an etching solution containing and [[oxidizing agent]] and [[hydrofluoric acid]]. The metal on the surface catalyzes the reduction of the oxidizing agent and therefore in turn also the dissolution of silicon. In the majority of the conducted research this phenomenon of increased dissolution rate is also spatially confined, such that it is increased in close proximity to a metal particle at the surface. Eventually this leads to the formation of straight pores that are etched into the semiconductor (see figure to the right). This means that a pre-defined pattern of the metal on the surface can be directly transferred to a semiconductor substrate.<ref name=geyer>{{cite journal |last1=Huang |first1=Zhipeng |last2=Geyer |first2=Nadine |last3=Werner |first3=Peter |last4=de Boor |first4=Johannes |last5=Gösele |first5=Ulrich |title=Metal‐Assisted Chemical Etching of Silicon: A Review: In memory of Prof. Ulrich Gösele |journal=Advanced Materials |date=11 January 2011 |volume=23 |issue=2 |pages=285–308 |doi=10.1002/adma.201001784|pmid=20859941 |s2cid=205237664 }}</ref>

== History of development ==
MACE is a relatively new technology in semiconductor engineering and therefore it has yet to be a process that is used in industry. The first attempts of MACE consisted of a silicon wafer that was partially covered with aluminum and then immersed in an etching solution.<ref name=dimova>{{cite journal |last1=Dimova-Malinovska |first1=D |last2=Sendova-Vassileva |first2=M |last3=Tzenov |first3=N |last4=Kamenova |first4=M |title=Preparation of thin porous silicon layers by stain etching |journal=Thin Solid Films |date=April 1997 |volume=297 |issue=1–2 |pages=9–12 |doi=10.1016/S0040-6090(96)09434-5}}</ref> This material combination led to an increased etching rate compared to bare silicon. Often this very first attempt is also called galvanic etching instead of metal assisted chemical etching.{{cn|date=October 2023}}

Further research showed that a thin film of a noble metal deposited on a silicon wafer's surface can also locally increase the etching rate. In particular, it was observed that noble metal particles sink down into the material when the sample is immersed in an etching solution containing an oxidizing agent and [[hydrofluoric acid]] (see image in the introduction).<ref name=li>{{cite journal |last1=Li |first1=X. |last2=Bohn |first2=P. W. |title=Metal-assisted chemical etching in HF/H2O2 produces porous silicon |journal=Applied Physics Letters |date=16 October 2000 |volume=77 |issue=16 |pages=2572–2574 |doi=10.1063/1.1319191|doi-access=free }}</ref>  This method is now commonly called the metal assisted chemical etching of silicon.   
Other semiconductors were also successfully etched with MACE, such as [[silicon carbide]]<ref name=leitgeb>{{cite journal |last1=Leitgeb |first1=Markus |last2=Zellner |first2=Christopher |last3=Schneider |first3=Michael |last4=Schwab |first4=Stefan |last5=Hutter |first5=Herbert |last6=Schmid |first6=Ulrich |title=Metal assisted photochemical etching of 4H silicon carbide |journal=Journal of Physics D: Applied Physics |date=1 November 2017 |volume=50 |issue=43 |pages=435301 |doi=10.1088/1361-6463/aa8942|doi-access=free }}</ref> or [[gallium nitride]].<ref name=diaz>{{cite journal |last1=Dı́az |first1=Diego J. |last2=Williamson |first2=Todd L. |last3=Adesida |first3=Ilesanmi |last4=Bohn |first4=Paul W. |last5=Molnar |first5=Richard J. |title=Morphology evolution and luminescence properties of porous GaN generated via Pt-assisted electroless etching of hydride vapor phase epitaxy GaN on sapphire |journal=Journal of Applied Physics |date=15 December 2003 |volume=94 |issue=12 |pages=7526–7534 |doi=10.1063/1.1628833}}</ref> However, the main portion of research is dedicated to MACE of silicon.

It has been shown that both [[noble metal]]s such as [[gold]],<ref>{{cite journal |last1=Mikhael |first1=Bechelany |last2=Elise |first2=Berodier |last3=Xavier |first3=Maeder |last4=Sebastian |first4=Schmitt |last5=Johann |first5=Michler |last6=Laetitia |first6=Philippe |title=New Silicon Architectures by Gold-Assisted Chemical Etching |journal=ACS Applied Materials & Interfaces |date=26 October 2011 |volume=3 |issue=10 |pages=3866–3873 |doi=10.1021/am200948p|pmid=21882843 }}</ref> [[platinum]],<ref>{{cite journal |last1=Tsujino |first1=Kazuya |last2=Matsumura |first2=Michio |title=Helical Nanoholes Bored in Silicon by Wet Chemical Etching Using Platinum Nanoparticles as Catalyst |journal=Electrochemical and Solid-State Letters |date=2005 |volume=8 |issue=12 |pages=C193 |doi=10.1149/1.2109347}}</ref> [[palladium]], <ref>{{cite journal |last1=Chen |first1=Jun-Ming |last2=Chen |first2=Chia-Yuan |last3=Wong |first3=C.P. |last4=Chen |first4=Chia-Yun |title=Inherent formation of porous p-type Si nanowires using palladium-assisted chemical etching |journal=Applied Surface Science |date=January 2017 |volume=392 |pages=498–502 |doi=10.1016/j.apsusc.2016.09.048}}</ref> and [[silver]],<ref>{{cite journal |last1=Lee |first1=Jung-In |last2=Park |first2=Soojin |title=High-performance porous silicon monoxide anodes synthesized via metal-assisted chemical etching |journal=Nano Energy |date=January 2013 |volume=2 |issue=1 |pages=146–152 |doi=10.1016/j.nanoen.2012.08.009}}</ref> and [[base metal]]s such as [[iron]],<ref>{{cite journal |last1=Loni |first1=A. |last2=Barwick |first2=D. |last3=Batchelor |first3=L. |last4=Tunbridge |first4=J. |last5=Han |first5=Y. |last6=Li |first6=Z. Y. |last7=Canham |first7=L. T. |title=Extremely High Surface Area Metallurgical-Grade Porous Silicon Powder Prepared by Metal-Assisted Etching |journal=Electrochemical and Solid-State Letters |date=1 May 2011 |volume=14 |issue=5 |pages=K25–K27 |doi=10.1149/1.3548513|doi-access=free }}</ref> [[nickel]],<ref name=":0">{{cite journal |last1=Volovlikova |first1=Olga V. |last2=Gavrilov |first2=S.A. |last3=Lazarenko |first3=P.I. |last4=Kukin |first4=A.V. |last5=Dudin |first5=A.A. |last6=Tarhanov |first6=A.K. |title=Influence of Etching Regimes on the Reflectance of Black Silicon Films Formed by Ni-Assisted Chemical Etching |journal=Key Engineering Materials |date=June 2019 |volume=806 |pages=24–29 |doi=10.4028/www.scientific.net/KEM.806.24|s2cid=197607732 }}</ref><ref name=":1">{{cite journal |last1=Azeredo |first1=B P |last2=Sadhu |first2=J |last3=Ma |first3=J |last4=Jacobs |first4=K |last5=Kim |first5=J |last6=Lee |first6=K |last7=Eraker |first7=J H |last8=Li |first8=X |last9=Sinha |first9=S |last10=Fang |first10=N |last11=Ferreira |first11=P |last12=Hsu |first12=K |title=Silicon nanowires with controlled sidewall profile and roughness fabricated by thin-film dewetting and metal-assisted chemical etching |journal=Nanotechnology |date=7 June 2013 |volume=24 |issue=22 |pages=225305 |doi=10.1088/0957-4484/24/22/225305|pmid=23644697 |s2cid=6072818 }}</ref> [[copper]],<ref>{{cite journal |last1=Qiu |first1=Teng |last2=Chu |first2=Paul K. |title=Self-selective electroless plating: An approach for fabrication of functional 1D nanomaterials |journal=Materials Science and Engineering: R: Reports |date=May 2008 |volume=61 |issue=1–6 |pages=59–77 |doi=10.1016/j.mser.2008.03.001}}</ref> and [[aluminium]]<ref>{{cite journal |last1=Uddin |first1=Shahnawaz |last2=Hashim |first2=Md Roslan |last3=Pakhuruddin |first3=Mohd Zamir |title=Aluminium-assisted chemical etching for fabrication of black silicon |journal=Materials Chemistry and Physics |date=June 2021 |volume=265 |pages=124469 |doi=10.1016/j.matchemphys.2021.124469|s2cid=233542194 }}</ref> can act as a [[catalyst]] in the process.

== Theory ==
[[File:Mace mechanism.png|thumb|Depiction of the mechanism of MACE: The reduction of an oxidizing agent (in this case H<sub>2</sub>O<sub>2</sub>) is catalyzed at the surface of a noble metal nanoparticle (in this case gold). Because of this, holes (h<sup>+</sup>) are injected into the valence band of the silicon substrate. These holes weaken chemical bonds at the silicon/etching solution interface and thus dissolution of the substrate with HF takes place.]]
Some elements of MACE are commonly accepted in the scientific community, while others are still under debate.<ref name=geyer/> There is agreement that the reduction of the oxidizing agent is catalyzed by the noble metal particle (see figure to the left). This means that the metal particle has a surplus of positive charge which is eventually transferred to the silicon substrate. Each of the positive charges in the substrate can be identified as a hole (h<sup>+</sup>) in the [[valence band]] of the substrate, or in more chemical terms it may be interpreted as a weakened Si-Si bond due to the removal of an electron. 
The weakened bonds can be attacked by a [[Nucleophile|nucleophilic species]] such as HF or H<sub>2</sub>O, which in turn leads to the dissolution of the silicon substrate in close proximity to the noble metal particle. {{Citation needed|date=October 2023}}

From a thermodynamic point of view, the MACE process is possible because the [[redox potential]] of the redox couple corresponding to the used oxidizing agents ([[hydrogen peroxide]] or [[potassium permanganate]]) are below the valence band edge at the electrochemical energy scale. Equivalently, one could say that the [[electrochemical potential]] of the [[electron]] in the etching solution (due to the presence of oxidizing agent) is lower than the electrochemical potential of the electron in the substrate, hence electrons are removed from the silicon. In the end, this accumulation of positive charge leads to the dissolution of the substrate by hydrofluoric acid.<ref name=geyer/>

MACE consists of multiple individual reactions. At the metal particle, the oxidizing agent is reduced. In the case of hydrogen peroxide this can be written down as follows:

:<chem>H2O2 + 2H+ -> 2H2O + 2h+</chem>

The created holes (h<sup>+</sup>) are then consumed during the dissolution of silicon. There are several possible reactions via which the dissolution can take place, but here just one example is given:

:<chem>Si + 6HF + 4h+ -> SiF6^{2}- + 6H+</chem>

There are still some unclear aspects of the MACE process. The model proposed above requires contact of the metal particle with the silicon substrate which is somehow conflicting with the etching solution being underneath the particle. This can be explained with a dissolution and redeposition of metal during MACE. In particular it is proposed, that some metal ions from the particle are dissolved and eventually are re-deposited at the silicon surface with a redox reaction. In this case the metal particle (or even larger noble metal thin films) could partially maintain contact to the substrate while also etching could partially take place underneath the metal.<ref name=geyer2>{{cite journal |last1=Geyer |first1=Nadine |last2=Fuhrmann |first2=Bodo |last3=Huang |first3=Zhipeng |last4=de Boor |first4=Johannes |last5=Leipner |first5=Hartmut S. |last6=Werner |first6=Peter |title=Model for the Mass Transport during Metal-Assisted Chemical Etching with Contiguous Metal Films As Catalysts |journal=The Journal of Physical Chemistry C |date=21 June 2012 |volume=116 |issue=24 |pages=13446–13451 |doi=10.1021/jp3034227}}</ref>

It is also observed that in the vicinity of straight pores as shown in the introduction also a micro-porous region between the pores is formed. Generally this is attributed to holes that diffuse away from the particle and hence contribute to etching at more distant locations.<ref name="li2">{{cite journal |last1=Li |first1=Xiuling |title=Metal assisted chemical etching for high aspect ratio nanostructures: A review of characteristics and applications in photovoltaics |journal=Current Opinion in Solid State and Materials Science |date=April 2012 |volume=16 |issue=2 |pages=71–81 |doi=10.1016/j.cossms.2011.11.002}}</ref>
This behavior is dependent on the doping type of substrate as well as on the type of noble metal particle. Therefore, it is proposed that the formation of such a porous region beneath the straight pores depends on the type of barrier that is formed at the metal/silicon interface. In the case of an upward [[band bending]] the electric field in the [[depletion layer]] would point towards the metal. Therefore, holes cannot diffuse further into the substrate and thus no formation of a micro-porous region is observed. In the case of downward band-bending holes could escape into the bulk of the silicon substrate and eventually lead to etching there.<ref name="ruby">{{cite journal |last1=Lai |first1=Ruby A. |last2=Hymel |first2=Thomas M. |last3=Narasimhan |first3=Vijay K. |last4=Cui |first4=Yi |title=Schottky Barrier Catalysis Mechanism in Metal-Assisted Chemical Etching of Silicon |journal=ACS Applied Materials & Interfaces |date=13 April 2016 |volume=8 |issue=14 |pages=8875–8879 |doi=10.1021/acsami.6b01020|pmid=27018712 |osti=1579822 }}</ref>

== Experimental procedure of MACE ==
[[File:Mace particles.png|thumb|Silver nanoparticles at the surface of a silicon wafer after immersion into a solution containing [[silver nitrate]] and hydrofluoric acid.]]
As already stated above MACE requires metal particles or a thin metal thin film on top of a silicon substrate. This can be achieved with several methods such as [[sputter deposition]] or [[Evaporation (deposition)|thermal evaporation]].<ref name = kabalan>Kabalan, Amal. "A Comparative Study on the Effects of Passivation Methods on the Carrier Lifetime of RIE and MACE Silicon Micropillars." Applied Sciences 9.9 (2019): 1804.</ref> A method to obtain particles from a continuous thin film is thermal [[dewetting]].<ref name = backes>Backes, A., et al. "Influence of metallic catalyst and doping level on the metal assisted chemical etching of silicon." Scripta Materialia 114 (2016): 27-30.</ref>
These deposition methods can be combined with [[Photolithography|lithography]]<ref name = chang>Chang, Shih‐Wei, et al. "Densely packed arrays of ultra‐high‐aspect‐ratio silicon nanowires fabricated using block‐copolymer lithography and metal‐assisted etching." Advanced functional materials 19.15 (2009): 2495-2500.</ref> such that only desired regions are covered with metal. Since MACE is an anisotropic etching method (etching takes place not in all spatial directions) a pre-defined metal pattern can be directly transferred into the silicon substrate.
Another method of depositing metal particles or thin films is [[electroless plating]] of noble metals on the surface of silicon. Since the redox potentials of the redox couples of noble metals are below the valence band edge of silicon, noble metal ions can (like described in the theory section) inject holes (or extract electrons) from the substrate while they are reduced. In the end metallic particles or films are obtained at the surface.<ref name = smith>Smith, Zachary R., Rosemary L. Smith, and Scott D. Collins. "Mechanism of nanowire formation in metal assisted chemical etching." Electrochimica Acta 92 (2013): 139-147.</ref>
Finally, after the deposition of the metal on the surface of silicon, the sample is immersed in an etching solution containing hydrofluoric acid and oxidizing agent. Etching will take place as long as the oxidizing agent and the acid are consumed or until the sample is removed from the etching solution.

== Applications of MACE ==
[[File:Etch anisotropy.png|thumb|164x164px|Schematic depiction of a silicon substrate that is covered with a protective layer (red). 1: Wet chemical etching leads to isotropic etching 2: Etching methods that operate in the gas-phase allow anisotropic etching but are expensive.]]
The reason why MACE is heavily researched is that it allows completely anisotropic etching of silicon substrates which is not possible with other wet chemical etching methods (see figure to the right). Usually the silicon substrate is covered with a protective layer such as [[photoresist]] before it is immersed in an etching solution. The etching solution usually has no preferred direction of attacking the substrate, therefore isotropic etching takes place. In semiconductor engineering, however it is often required that the sidewalls of the etched trenches are steep. This is usually realized with methods that operate in the gas-phase such as [[reactive ion etching]]. These methods require expensive equipment compared to simple wet etching. MACE, in principle allows the fabrication of steep trenches but is still cheap compared to gas-phase etching methods.

=== Porous silicon ===
Metal assisted chemical etching allows for the production of [[porous silicon]] with [[photoluminescence]].<ref name=li/>

=== Black silicon ===
[[Black silicon]] is silicon with a modified surface and is a type of [[porous silicon]]. There are several works{{Clarification needed|reason=|date=September 2019}} on obtaining [[black silicon]] using MACE technology. The main application of black silicon is [[solar energy]].<ref name=":0" /><ref name=":1" />

=== Black Gallium Arsenide ===
Black Gallium Arsenide with light trapping properties have been also produced by MACE.<ref>{{cite journal |last1=Lova |first1=Paola |first2=Valentina |last2=Robbiano |first3=Franco |last3=Cacialli |first4=Davide |last4=Comoretto |first5=Cesare |last5=Soci|title=Black GaAs by Metal-Assisted Chemical Etching |journal=ACS Applied Materials & Interfaces |date=2018 |volume=10 |issue=39 |pages=33434–33440 |doi=10.1021/acsami.8b10370 |pmid=30191706 |doi-access=free}}</ref>

== References ==
{{reflist}}

[[Category:Etching]]
[[Category:Chemistry]]
[[Category:Research lasers]]
[[Category:Semiconductors]]
[[Category:Engineering]]